The effect of repair protocols and chewing simulation on the microtensile bond strength of two resin matrix ceramics to composite resin.

BACKGROUND: To assess the micro tensile bond strength (µTBS) of two resin matrix ceramic (RMC) blocks bonded to composite resin by using different repair protocols with and without chewing simulation (CS). MATERIALS AND METHODS: Two resin matrix ceramic blocks (Vita Enamic and Lava Ultimate) were divided into 4 groups according to the surface treatments: Bur grinding (control), Bur grinding + silane, 9.5% HF acid etching, and 9.5% HF acid etching + silane. The single bond universal adhesive was applied on all specimens after the surface treatments according to the manufacturer's instructions, it was administered actively on the treated surface for 20 s and then light cured for 10 s, followed by incremental packing of composite resin to the treated surface. Each group was further divided into 2 subgroups (with/without chewing simulation for 500,000 cycles). A micro tensile bond strength test was performed for each group (n = 15). The effect of surface treatments on the materials was examined by using a scanning electron microscope (SEM). The micro tensile bond strength (MPa) data were analyzed with a three-way ANOVA, the independent t-test, and one-way ANOVA followed by the Tukey post-hoc test. RESULTS: µTBS results were significantly higher for Lava Ultimate than Vita Enamic for all the surface treatment protocols with (p < 0.01). The chewing simulation significantly negatively affected the micro-tensile bond strength (p < 0.001). Bur grinding + saline exhibited the highest bond strength values for Lava Ultimate, both with and without chewing simulation. For Vita Enamic, bur grinding + saline and HF acid + saline showed significantly higher bond strength values compared to other surface treatments, both with and without chewing simulation (p ≤ 0.05). CONCLUSION: Bur grinding + silane could be recommended as a durable repair protocol for indirect resin matrix ceramics blocks with composite resin material.

Effect of silanization of poly (urea-formaldehyde) microcapsules on the flexural strength and self-healing efficiency of an experimental self-healing dental resin composite (An in-vitro study).

OBJECTIVES: This study investigated the impact of using γ-methacryloxypropyl trimethoxy silane (MPS) for surface silanization of poly (urea-formaldehyde) (PUF) microcapsules which enclose a healing liquid of "triethylene glycol dimethacrylate (TEGDMA) and N,N dihydroxyethyl-p-toluidine (DHEPT)" on some mechanical properties of an experimental dental composite as well as its self-healing efficiency. METHODS: Synthesis of PUF microcapsules was done via in situ polymerization, followed by silanization with MPS silane. Silanized and non-silanized microcapsules were incorporated into a composite containing 30% polymer matrix and 70% fillers at different weight percentages (0%, 5%, 7.5% and 10%). The composite strength and elastic modulus were evaluated by Flexural testing. Fracture toughness KIc and self-healing efficiency were assessed by utilizing the "single edge notched beam" method. RESULTS: Flexural strength of all groups containing silanized microcapsules was non-significantly different from control group without microcapsules. However, in contrast to control group, all groups containing non-silanized microcapsules displayed considerably decreased flexural strength. Adding silanized and non-silanized microcapsules didn't show a significant change in the KIc-virgin. The silanized microcapsules' groups achieved a self-healing efficiency of about 49-77% recovery in KIc-virgin compared to 38-69% for their non-silanized counterparts. SIGNIFICANCE: In order to increase the interfacial adhesion with the polymer matrix, improve the mechanical properties, and increase the efficiency of self-healing of dental resin composite, PUF microcapsules were silanized for the first time in the dental field using MPS silane. This innovative silanized microcapsule-containing self-healing composite may hold promise for repairing the damage caused by restorative cracks and extending their service life.